The EN 10219 S235JRH pipe is made in accordance with all applicable ASTM, ASME, and international standards. These pipes have greater corrosion resistance and are suitable for use in a variety of temperatures.


Cold-Formed S235JRH Steel Welded Pipe has tensile strengths ranging from 316Mpa to 510Mpa and yield strength of at least 235Mpa. These pipes may be readily extended by 26%. The S235JRH Tube is widely utilized in civil engineering applications such as bridge construction, structural frames, factory structures, and mechanical engineering systems.

Send Email

  • DESIGNATION FOR EN 10219 S235JRH STEEL GRADE

    • The number of this European Standard (EN 10219 specification);
    • The capital letter S for structural steel;
    • The indication of the minimum specified yield strength for thickness ≤16mm is expressed in N/mm2;
    • The capital letters JR for the qualities with specified impact properties at room temperature;
    • The capital letter J and a number 0 or 2 for the qualities with specified impact properties at 0℃ and -20℃ respectively;
    • The capital letter H indicates hollow sections

  • DIMENSIONS AND SIZES OF EN10219 S235JRH PIPE

    DN O. D. W. T.
    Inch mm SCH5S SCH10S SCH10 SCH20 SCH30 SCH40 SCH60 SCH80 SCH100 SCH120 SCH140 SCH160 STD XS XXS
    50 2″ 60.3 1.65 2.77 – – – 3.91 – 5.54 – – – 8.74 3.91 5.54 11.07
    65 2 1/2″ 73 2.11 3.05 – – – 5.16 – 7.01 – – – 9.53 5.16 7.01 14.02
    80 3″ 88.9 2.11 3.05 – – – 5.49 – 7.62 – – – 11.13 5.49 7.52 15.24
    90 3 1/2″ 101.6 2.11 3.05 – – – 5.74 – 8.08 – – – – 5.74 8.08 –
    100 4″ 114.3 2.11 3.05 – – – 6.02 – 8.58 – 11.13 – 13.49 6.02 8.56 17.12
    125 5″ 141.3 2.77 3.4 – – – 6.55 – 9.53 – 12.7 – 15.88 6.55 9.53 18.05
    150 6″ 168.3 2.77 3.4 – – – 7.11 – 10.97 – 14.27 – 18.26 7.11 10.97 21.95
    200 8″ 219.1 2.77 3.76 – 6.35 7.04 8.18 10.31 12.7 15.09 18.26 20.62 23.01 8.18 12.7 22.23
    250 10″ 273.1 3.4 4.19 – 6.35 7.8 9.27 12.7 15.09 18.26 21.44 25.4 28.58 9.27 12.7 25.4
    300 12″ 323.9 3.96 4.57 – 6.35 8.38 10.31 14.27 17.48 21.44 25.4 28.58 33.32 9.53 12.7 25.4
    350 14″ 355.5 3.96 4.78 6.35 7.92 9.53 11.13 15.09 19.05 23.83 27.79 31.75 35.71 9.53 12.7 –
    400 16″ 406.4 4.19 4.78 6.35 7.92 9.53 12.7 16.66 21.44 26.19 30.96 36.53 40.49 9.53 12.7 –
    450 18″ 457.2 4.19 4.78 6.35 7.92 11.13 14.27 19.05 23.83 39.36 34.93 39.67 45.24 – – –
    500 20″ 508 4.78 5.54 6.35 9.53 12.7 15.09 20.62 26.19 32.54 38.1 44.45 50.01 – – –
    550 22″ 558.8 4.78 5.54 6.35 9.53 12.7 – 22.23 28.58 34.93 41.28 47.63 53.98 – – –
    600 24″ 609.6 5.54 6.35 6.35 9.53 14.27 17.48 24.61 30.96 38.89 46.02 52.37 59.54 – – –

  • WELDABILITY OF EN 10219 S235JRH PIPE

    This European standard specifies weldable steel. EN 1011-1 and EN 1011-2 provide the essential specifications for welding items covered by this European standard.


    The greatest concern while welding these materials is the development of cold cracking in the welded zone as the thickness, strength level, and CEV of the product increase. Cold cracking occurs as a result of the following factors:

      • Enhanced diffusible hydrogen concentrations in the weld metal;
      • Brittle structure in the heat-affected zone;
      • High tensile stress concentrations in the welded joint

  • CHEMICAL COMPOSITION OF S235JRH FOR PRODUCT THICKNESSES ≤ 40 MM (HEAT ANALYSIS IN %)

    Steel grade Material number Type of deoxidation1) C Si Mn P S N2)
    S235JRH 1.0039 FF ≤ 0,17 – ≤ 1,40 ≤ 0,040 ≤ 0,040 ≤ 0,009
    FF = Fully killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e. g. min. 0,020 % total Al or 0,015 % soluble Al).
    The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % with a minimum Al/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in the Inspection Document.

  • MECHANICAL PROPERTIES OF S235JRH AT ROOM TEMPERATURE

    Steel Grade Material number
    Yield Strength ReH
    N/mm² min.
    for Nominal Wall Thickness in mm
    Tensile strength Rm
    N/mm²
    for Nominal Wall Thickness in mm
    Elongation A 4)
    %
    min.
    for Nominal Wall Thickness in mm
    Impact Energy KV5)
    J
    min.
    at a Temperature °C of
    ＜ 16
    > 16
    ≤ 40
    		< 3
    ≥ 3
    ≤40
    		≤40 -20 0 +20
    S235JRH1) 1.0039 235 225 360 -510 360 – 510 242) – – 27
    The impact test has to be proved only if option 1.3 is determined.
    For wall thicknesses > 3 mm and section sizes D/T < 15 (circular) and (B+H)/2T x 12,5 (square or rectangular) the minimum elongation is reduced by 2. For wall thicknesses £ 3 mm the minimum value for elongation is 17 %.
    For section sizes D/T < 15 (circular) and (B+H)/2T x 12,5 (square or rectangular) the minimum elongations are reduces by 2.
    For wall thickness below 3 mm see DIN EN 10219-1, 9.2.2.
    For impact tests with test pieces with reduced cross-section see DIN EN 10219-1, 6.7.2.

  • MANUFACTURING TOLERANCES OF EN 10219 S235JRH PIPE

    Characteristic Round Hollow Sections Square and Rectangular Hollow Sections
    Outside Dimension ± 1% with min ± 0.5mm and max ± 10mm ± 1% with min of ± 0.5mm
    Thickness (T) T≤5mm: ±10% T≤5mm: ±10%
    T>5mm: ± 0.5mm T>5mm: ± 0.5mm
    Out-of-Roundness 2% –
    Convexity – Max .8% with min 0.5mm
    Squareness of side – 90° ± 1°
    External Corner Profile – T≤6mm: 1.6T to 2.4T
    – 6<T≤10mm: 2.0T to 3.0T
    – T,10: 2.4T to 3.6T
    Twist – 2mm plus 0.5mm/m
    Straightness 0.2% of total 0.15% of total
    Mass ±6% on individual length

  • INSPECTION AND TESTING OF EN 10219 S235JRH HOLLOW SECTIONS OF NON-ALLOY STEELS

    EN 10219 S235JRH is tensile tested according to EN 10002-1 and Charpy impact tested according to EN 10045-1.


    Inspection Requirements Inspection Frequency
    Type of test
    Non-specific
    inspection
    		Specific inspection
    Mandatory
    tests     		1 Cast analysis One result per delivery
    item     		One per cast
    2 Tensile test One result per delivery
    item     		One per test unit ( b)
    3 Impact test for
    Qualities J2 and K2 only     		Not applicable One set per test unit (b)
    4 Surface condition
    and dimensions     		– –
    5 NDT of the weld Not applicable All products, full length
    Optional
    tests     		6 Product analysis Not applicable One per test unit a
    7 Cast analysis
    additional elements     		Not applicable See Option 1.2
    8 Impact test for
    qualities JR and J0     		Not applicable One set per test unit (b)
    b – Longitudinal or transverse samples at the discretion of the manufacturer.

Follow us   facebook instagram twitter youtube linkedin

H-beam,Galvanized Seamless Pipe,External Polyethylene Coating pipe

LEAVE A MESSAGE HERE

Products

Workshop

Copyright @ 2023 Union Steel Industry Co.,Ltd All Rights Reserved Privacy Policy
We use cookies and other tracking technologies to improve your browsing experience on our website, to show you personalized content and targeted ads, to analyze our website traffic, and to understand where our visitors are coming from.
Accept
Decline